One Part Waterborne Epoxy Ester Resin Iron Oxide Coating Resin Brown Viscous Liquid

Products

Solvent Based Solid Acrylic Resin

2K Epoxy Resin and Curing Agents

Water Based Polyurethane Dispersions

Mr. jax

jax@wangqinresins.com

86-592-5796106

Contact Now

One Part Waterborne Epoxy Ester Resin Iron Oxide Coating Resin Brown Viscous Liquid

MOQ:	5000kg
Price:	Negotiable
Payment Method:	L/C,T/T
Supply Capacity:	500t/month

Details Information

Product Description

Detail Information

Place of Origin

China

Brand Name

WeiLi Resin®

Certification

ISO9001

Model Number

WL-172B

Product Name:

One Component Waterborne Epoxy Ester Resin For Red Oxide Primer And Topcoat

Appearance:

Brown Viscous Liquid

Non-Volatile Matter ( %):

74±2.0

Viscosity (25℃， MPa.s):

Highlight:

One Part Waterborne Epoxy Ester Resin

Iron Oxide Coating Resin Liquid

Product Description

A red iron oxide primer and topcoat formulated with water-soluble epoxy ester resin WL-172B features a high-performance, single-component, quick-drying, rust-preventive composition designed for application on ferrous metal substrates. This versatile coating delivers corrosion protection for both indoor and outdoor steel surfaces while maintaining enduring resistance to rust and degradation across diverse metal applications. It is compatible with various top-coatings, including water-based and alkyd/oil-based finishes. The primer exhibits exceptional hide properties, smooth application, sag resistance, abrasion resistance, and unmatched durability.

Product Properties:

▲ Self-emulsifying process, no emulsifier, excellent water resistance and corrosion resistance;

▲ This product can be oxidized and cross-linked to form film, which can replace the traditional solvent based alkyd and epoxy ester resin;

▲ Paint making process is similar to that of traditional solvent based paint, the resin can be grinded;

▲ Good mechanical stability and storage stability.

Resin Composition:

Waterborne resin, cosolvent, neutralizer

Typical Data:

Item	WL-172B	Test Method
Appearance	Brown viscous liquid	Visual Observation
Non-Volatile Matter ( %)	74±2.0	GB/T1725-2007 ( 30min@120℃)
Viscosity (25℃, mPa.s)	≤200	GB/T 21059-2007 NDJ-79 Rotational Viscometer Dilute with PM by 1:1 ratio, then test

Recommending WL-172B high performance waterborne epoxy ester resin

WL-172B Iron Oxide Red Primer

Reference Formula:

1	WL-172B
2	N,N-DMEA
3	Deionized Water
4	Dispersing Agent
5	Defoamer
6	Attapulgite
7	Iron Oxide Red
8	Zinc Sulphate
9	Precipitated Barium Sulphate
10	Deionized Water
11	WL-172B
12	N,N-DMEA
13	Drier
14	Sodium Nitrite
15	Deionized Water
16	Substrate Wetting Agent
17	Thickener

Performance Data:

No.	Test Item	Test Data	Test Standard
1	Original Paint Appearance	No lumps, stir evenly	Visual Observation
2	Paint Film Color	Iron red color	Visual Observation
3	Original Paint Viscosity(25℃)Ku	80-90	GB/T9269-2009
4	pH	8-9	GB8325-1987
5	Fineness μm	＜35	GB/T6753.1-2007
6	Non-Volatile Matter Content %	48	GB/T1725-2007
7	Surface Drying Time	≤20min	GB1728-79
8	Hard Drying Time	≤5hrs	GB1728-79
9	Gloss	10	GB/T9754-2007
10	Hardness (Pencil Method)	HB	GB/T6739-1996
11	Flexibility	1mm	GB/T6742-2007
12	Impact Resistance kg.cm	50	GB/T1732-1993
13	Double Pendulum Hardness	0.58	GB/T1730-2007
14	Adhesion (Cross-Cut Method)	1grade	GB/T9286-1998
15	Storage Stability	50℃*4 weeks,no layering, no sedimentation	————

Iron Oxide Red Primer Initial Water Resistance

Substrate:tinplate

Film thickness:23±3μm

Time	Water Drenching Test Data
Air Drying 24hrs	48hrs no abnormalities
Air Drying 72hrs	96hrs no abnormalities
Air Drying 168hrs	168hrs no abnormalities

Iron Oxide Red Primer Anti- Corrosive Properties

Substrate:carbon steel plate

Film thickness:45±5μm

Item	Test Data
Salt fog resistance	72hrs no abnormalities
Salt water resistance	120hrs no abnormalities

Resistant to Salt Fog for 48 hours

One Part Waterborne Epoxy Ester Resin Iron Oxide Coating Resin Brown Viscous Liquid 0

Resistant to Salt Fog for 96 hour

One Part Waterborne Epoxy Ester Resin Iron Oxide Coating Resin Brown Viscous Liquid 1

Resistant to Salt Fog for 144 hours

One Part Waterborne Epoxy Ester Resin Iron Oxide Coating Resin Brown Viscous Liquid 2

Resistant to Salt Water for 120 hours

One Part Waterborne Epoxy Ester Resin Iron Oxide Coating Resin Brown Viscous Liquid 3

Resistant to Salt Water for 144 hours

One Part Waterborne Epoxy Ester Resin Iron Oxide Coating Resin Brown Viscous Liquid 4

WL-172B Iron Oxide Red Primer

Reference Formula:

1	WL-172B
2	N,N-DMEA
3	Deionized Water
4	Dispersing Agent
5	Defoamer
6	Attapulgite
7	Titanium Dioxide
8	Carbon Black
9	Precipitated Barium Sulphate
10	Deionized Water
11	WL-172B
12	N,N-DMEA
13	Drier
14	Deionized Water
15	Substrate Wetting Agent
16	Thickener

Performance Data:

No.	Test Item	Test Data	Test Standard
1	Original Paint Appearance	No lump, stir evenly	Visual Observation
2	Paint Film Color	Gray	Visual Observation
3	Original Paint Viscosity(25℃)Ku	80-90	GB/T9269-2009
4	pH	8-9	GB8325-1987
5	Fineness μm	＜30	GB/T6753.1-2007
6	Non-Volatile Matter Content %	48	GB/T1725-2007
7	Surface Drying Time	≤3min	GB1728-79
8	Hard Drying Time	≤16hrs	GB1728-79
9	Gloss	90-92	GB/T9754-2007
10	Hardness(pencil method)	HB	GB/T6739-1996
11	Flexibility	1mm	GB/T6742-2007
12	Impact Resistance kg.cm	50	GB/T1732-1993
13	Double Pendulum Hardness	0.4	GB/T1730-2007
14	Adhesion(Cross-Cut Method)	1grade	GB/T9286-1998

High Gloss Gray Topcoat Hardness Increase

Substrate:glass pane

Film thickness:23±3μm

Ambient temperature:25±5℃

Ambient humidity:50±2%

Double Pendulum Hardness(glass pane)
Time	Drier 0.52%	Drier 0.85%
24hrs	0.19	0.22
48hrs	0.25	0.27
72hrs	0.28	0.32
120hrs	0.53	0.53

High Gloss Gray Topcoat Initial Water Resistance

Substrate:tinplate

Film thickness:23±3μm

Time	Water drenching before adjustment	Water drenching after adjustment
Air Drying 24hrs	24hrs no abnormalities	48hrs no abnormalities
Air Drying 72hrs	44hrs no abnormalities	56hrs no abnormalities
Air Drying 168hrs	96hrs no abnormalities	144hrs no abnormalities

Tags:

Epoxy Modified Acrylic Emulsion,

Industrial Coating Resin,

Epoxy Ester Resin

1K Industrial Coating Resins Single Component Water Soluble Epoxy Ester Resin 200kg/Drum

Contact Now

One Component Waterborne Epoxy Ester Resin Water Resistant Industrial Coating Resin

Contact Now

Fast Drying Water Based Epoxy Modified Acrylic Emulsion For Metal Surface Protection Paints

Contact Now

Eco Friendly Waterborne Acrylic Resin Epoxy Ester Coating Dispersion Formula

Contact Now

PRODUCTS DETAILS

Products

Solvent Based Solid Acrylic Resin

Waterborne Acrylic Resin

Wax Additive

Hydroxyl Acrylic Resin

2K Epoxy Resin and Curing Agents

Saturated Polyester Resin

Alkyd Resin

1K Industrial Coating Resins

Water Based Polyurethane Dispersions

One Part Waterborne Epoxy Ester Resin Iron Oxide Coating Resin Brown Viscous Liquid

MOQ:	5000kg
Price:	Negotiable
Payment Method:	L/C,T/T
Supply Capacity:	500t/month

Detail Information

Product Description

Detail Information

Place of Origin

China

Brand Name

WeiLi Resin®

Certification

ISO9001

Model Number

WL-172B

Product Name:

One Component Waterborne Epoxy Ester Resin For Red Oxide Primer And Topcoat

Appearance:

Brown Viscous Liquid

Non-Volatile Matter ( %):

74±2.0

Viscosity (25℃， MPa.s):

≤200

Minimum Order Quantity:

5000kg

Price:

Negotiable

Payment Terms:

L/C,T/T

Supply Ability:

500t/month

Highlight

One Part Waterborne Epoxy Ester Resin

Iron Oxide Coating Resin Liquid

Product Description

Product Properties:

▲ Self-emulsifying process, no emulsifier, excellent water resistance and corrosion resistance;

▲ This product can be oxidized and cross-linked to form film, which can replace the traditional solvent based alkyd and epoxy ester resin;

▲ Paint making process is similar to that of traditional solvent based paint, the resin can be grinded;

▲ Good mechanical stability and storage stability.

Resin Composition:

Waterborne resin, cosolvent, neutralizer

Typical Data:

Item	WL-172B	Test Method
Appearance	Brown viscous liquid	Visual Observation
Non-Volatile Matter ( %)	74±2.0	GB/T1725-2007 ( 30min@120℃)
Viscosity (25℃, mPa.s)	≤200	GB/T 21059-2007 NDJ-79 Rotational Viscometer Dilute with PM by 1:1 ratio, then test

Recommending WL-172B high performance waterborne epoxy ester resin

WL-172B Iron Oxide Red Primer

Reference Formula:

1	WL-172B
2	N,N-DMEA
3	Deionized Water
4	Dispersing Agent
5	Defoamer
6	Attapulgite
7	Iron Oxide Red
8	Zinc Sulphate
9	Precipitated Barium Sulphate
10	Deionized Water
11	WL-172B
12	N,N-DMEA
13	Drier
14	Sodium Nitrite
15	Deionized Water
16	Substrate Wetting Agent
17	Thickener

Performance Data:

No.	Test Item	Test Data	Test Standard
1	Original Paint Appearance	No lumps, stir evenly	Visual Observation
2	Paint Film Color	Iron red color	Visual Observation
3	Original Paint Viscosity(25℃)Ku	80-90	GB/T9269-2009
4	pH	8-9	GB8325-1987
5	Fineness μm	＜35	GB/T6753.1-2007
6	Non-Volatile Matter Content %	48	GB/T1725-2007
7	Surface Drying Time	≤20min	GB1728-79
8	Hard Drying Time	≤5hrs	GB1728-79
9	Gloss	10	GB/T9754-2007
10	Hardness (Pencil Method)	HB	GB/T6739-1996
11	Flexibility	1mm	GB/T6742-2007
12	Impact Resistance kg.cm	50	GB/T1732-1993
13	Double Pendulum Hardness	0.58	GB/T1730-2007
14	Adhesion (Cross-Cut Method)	1grade	GB/T9286-1998
15	Storage Stability	50℃*4 weeks,no layering, no sedimentation	————

Iron Oxide Red Primer Initial Water Resistance

Substrate:tinplate

Film thickness:23±3μm

Time	Water Drenching Test Data
Air Drying 24hrs	48hrs no abnormalities
Air Drying 72hrs	96hrs no abnormalities
Air Drying 168hrs	168hrs no abnormalities

Iron Oxide Red Primer Anti- Corrosive Properties

Substrate:carbon steel plate

Film thickness:45±5μm

Item	Test Data
Salt fog resistance	72hrs no abnormalities
Salt water resistance	120hrs no abnormalities

Resistant to Salt Fog for 48 hours

One Part Waterborne Epoxy Ester Resin Iron Oxide Coating Resin Brown Viscous Liquid 0

Resistant to Salt Fog for 96 hour

One Part Waterborne Epoxy Ester Resin Iron Oxide Coating Resin Brown Viscous Liquid 1

Resistant to Salt Fog for 144 hours

One Part Waterborne Epoxy Ester Resin Iron Oxide Coating Resin Brown Viscous Liquid 2

Resistant to Salt Water for 120 hours

One Part Waterborne Epoxy Ester Resin Iron Oxide Coating Resin Brown Viscous Liquid 3

Resistant to Salt Water for 144 hours

One Part Waterborne Epoxy Ester Resin Iron Oxide Coating Resin Brown Viscous Liquid 4

WL-172B Iron Oxide Red Primer

Reference Formula:

1	WL-172B
2	N,N-DMEA
3	Deionized Water
4	Dispersing Agent
5	Defoamer
6	Attapulgite
7	Titanium Dioxide
8	Carbon Black
9	Precipitated Barium Sulphate
10	Deionized Water
11	WL-172B
12	N,N-DMEA
13	Drier
14	Deionized Water
15	Substrate Wetting Agent
16	Thickener

Performance Data:

No.	Test Item	Test Data	Test Standard
1	Original Paint Appearance	No lump, stir evenly	Visual Observation
2	Paint Film Color	Gray	Visual Observation
3	Original Paint Viscosity(25℃)Ku	80-90	GB/T9269-2009
4	pH	8-9	GB8325-1987
5	Fineness μm	＜30	GB/T6753.1-2007
6	Non-Volatile Matter Content %	48	GB/T1725-2007
7	Surface Drying Time	≤3min	GB1728-79
8	Hard Drying Time	≤16hrs	GB1728-79
9	Gloss	90-92	GB/T9754-2007
10	Hardness(pencil method)	HB	GB/T6739-1996
11	Flexibility	1mm	GB/T6742-2007
12	Impact Resistance kg.cm	50	GB/T1732-1993
13	Double Pendulum Hardness	0.4	GB/T1730-2007
14	Adhesion(Cross-Cut Method)	1grade	GB/T9286-1998

High Gloss Gray Topcoat Hardness Increase

Substrate:glass pane

Film thickness:23±3μm

Ambient temperature:25±5℃

Ambient humidity:50±2%

Double Pendulum Hardness(glass pane)
Time	Drier 0.52%	Drier 0.85%
24hrs	0.19	0.22
48hrs	0.25	0.27
72hrs	0.28	0.32
120hrs	0.53	0.53

High Gloss Gray Topcoat Initial Water Resistance

Substrate:tinplate

Film thickness:23±3μm

Time	Water drenching before adjustment	Water drenching after adjustment
Air Drying 24hrs	24hrs no abnormalities	48hrs no abnormalities
Air Drying 72hrs	44hrs no abnormalities	56hrs no abnormalities
Air Drying 168hrs	96hrs no abnormalities	144hrs no abnormalities

Tags: